OD (mm) | Wand (mm) | Temperament | Maximaler Arbeitsdruckbalken bis 65oC | Dickentoleranz | Durchmessertoleranz Mittelwert | Durchmessertoleranz einschließlich Ovalität |
12 | 0.6 (TX) | Halb schwer | 63 | ± 10% | ± 0.04mm | ± 0.09mm |
12 | 0.8 (TY) | Halb schwer | 87 | ± 10% | ± 0.04mm | ± 0.09mm |
15 | 0.7 (TX) | Halb schwer | 58 | ± 10% | ± 0.04mm | ± 0.09mm |
15 | 1.0 (TY) | Halb schwer | 87 | ± 13% | ± 0.04mm | ± 0.09mm |
22 | 0.9 (TX) | Halb schwer | 51 | ± 10% | ± 0.05mm | ± 0.10mm |
22 | 1.2 (TY) | Halb schwer | 69 | ± 15% | ± 0.05mm | ± 0.10mm |
28 | 0.9 (TX) | Halb schwer | 40 | ± 10% | ± 0.05mm | ± 0.10mm |
28 | 1.2 (TY) | Halb schwer | 55 | ± 15% | ± 0.05mm | ± 0.10mm |
35 | 1 | hart | 42 | ± 15% | ± 0.06mm | ± 0.07mm |
35 | 1.2 (TX) | Halb schwer | 42 | ± 10% | ± 0.06mm | ± 0.07mm |
35 | 1.5 (TY) | hart | 64 | ± 10% | ± 0.06mm | ± 0.11mm |
42 | 1 | hart | 35 | ± 15% | ± 0.06mm | ± 0.07mm |
42 | 1.2 (TX) | Halb schwer | 35 | ± 10% | ± 0.06mm | ± 0.11mm |
42 | 1.5 (TY) | hart | 53 | ± 10% | ± 0.06mm | ± 0.07mm |
54 | 1 | hart | 27 | ± 15% | ± 0.06mm | ± 0.07mm |
54 | 1.2 (TX) | Halb schwer | 27 | ± 10% | ± 0.06mm | ± 0.11mm |
54 | 2.0 (TY) | hart | 55 | ± 10% | ± 0.06mm | ± 0.07mm |
66.7 | 1.2 (TX) | hart | 26 | ± 15% | ± 0.07mm | ± 0.10mm |
66.7 | 2.0 (TY) | hart | 45 | ± 15% | ± 0.07mm | ± 0.10mm |
76.1 | 1.5 (TX) | hart | 29 | ± 15% | ± 0.07mm | ± 0.10mm |
76.1 | 2.0 (TY) | hart | 39 | ± 15% | ± 0.07mm | ± 0.10mm |
108 | 1.5 (TX) | hart | 20 | ± 15% | ± 0.07mm | ± 0.20mm |
108 | 2.5 (TY) | hart | 34 | ± 15% | ± 0.07mm | ± 0.20mm |
133 | 1.5 (TX) | hart | 16 | ± 15% | ± 0.20mm | ± 0.70mm |
159 | 2.0 (TX) | hart | 18 | ± 15% | ± 0.20mm | ± 0.70mm |
219 | 3.0 (TX) | hart | 20 | ± 15% | ± 0.60mm | ± 1.50mm |
Der Arbeitsdruck entspricht BS 2871: Teil 1: 1971